Corrosion resistance of high pressure torsion obtained commercially pure titanium in acidic solution
Dragana R. Barjaktarević
; Faculty of Technology and Metallurgy, University of Belgrade, Karnegijeva 4, 11000 Belgrade, Serbia
Ivana D. Dimić
; Faculty of Technology and Metallurgy, University of Belgrade, Karnegijeva 4, 11000 Belgrade, Serbia
Ivana Lj. Cvijović-Alagić
; Institute of Nuclear Sciences "Vinča", University of Belgrade, PO Box 522, 11001 Belgrade, Serbia
Đorđe N. Veljović
; Faculty of Technology and Metallurgy, University of Belgrade, Karnegijeva 4, 11000 Belgrade, Serbia
Marko P. Rakin
orcid.org/0000-0002-3965-0380
; Faculty of Technology and Metallurgy, University of Belgrade, Karnegijeva 4, 11000 Belgrade, Serbia
Sažetak
The enhancement of commercially pure titanium (cpTi) mechanical properties, which is required for its medical application, can be achieved by grain refinement obtained by severe plastic deformation. In addition to mechanical properties improvement, excellent corrosion resistance of ultrafine-grained (UFG) cpTi in contact with human body fluids is required. Therefore, the aim of this study was to estimate electrochemical behavior of UFG cpTi obtained by high pressure torsion (HPT) under a pressure of 7,8 GPa at room temperature and up to 5 rotations. Electrochemical measurements were performed in artificial saliva at 37°C in order to simulate oral environment, since development of UFG cpTi is primarily aimed for dental implant applications. Electrochemical behavior of UFG cpTi was investigated by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization. The obtained results indicate that HPT process, through significant grain size reduction, increases corrosion resistance of cpTi.
Ključne riječi
artificial saliva; corrosion resistance; electrochemical measurements; ultrafine-grained titanium