An investigation of boride layers growth kinetics on carbon steels
Andrijana Milinović
orcid.org/0000-0002-0767-3959
; J. J. Strossmayer University of Osijek, Mechanical Engineering Faculty in Slavonski Brod, Trg Ivane Brlić Mažuranić 2, 35000 Slavonski Brod, Croatia
Dragomir Krumes
; J. J. Strossmayer University of Osijek, Mechanical Engineering Faculty in Slavonski Brod, Trg Ivane Brlić Mažuranić 2, 35000 Slavonski Brod, Croatia
Radojka Marković
; J. J. Strossmayer University of Osijek, Mechanical Engineering Faculty in Slavonski Brod, Trg Ivane Brlić Mažuranić 2, 35000 Slavonski Brod, Croatia
Sažetak
Kinetics of boride layers formation on C15 and C70W2 carbon steels has been investigated in this paper. Pack boronizing was carried out in temperature range 870 ÷ 970 °C with durations 4 ÷ 8 h. Average thickness of boride layers obtained on C15 steel ranges was from 69,9 to 239,2 µm, and on C70W2 steel from 60,6 to 181,2 µm. Microhardness of boride layers was estimated by means of Vickers HV 0,1 method. It was determined that hardness values of Fe2B iron boride obtained on both steels were almost equal, and did not depend on temperature and duration of boronizing. Based on the average thickness of boride layers and through usage of classical kinetics method, values of activation energy and frequency factor were determined. Based on these values, practical empirical expressions for boronizing of C15 and C70W2, indicating the dependence of boride layer thickness on boronizing temperature and time, were derived.
Ključne riječi
activation energy; boride layer; boronizing; carbon steels; diffusion; kinetics