Metalurgija, Vol. 53 No. 2, 2014.
Izvorni znanstveni članak
Influence of heat treatment on properties of ti-nb alloys
L. Kunčicka
; VŠB – Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, Czech Republic
P. Štěpan
; VŠB – Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, Czech Republic
J. Kliber
; VŠB – Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, Czech Republic
I. Mamuzić
; Croatian Metallurgical Society, Zagreb, Croatia
Sažetak
Ti-Nb alloys are of a large potential for industrial, as well as biomedical utilisation. Oxygen content in the alloy is a parameter influencing its properties and cannot be neglected. The main focus of this paper is on observation of influence of annealing time on oxygen content in the structure of Ti – 20,7 (at.)% Nb alloy. Four groups of the samples were annealed at the temperature of 800 °C from 15 to 60 minutes with 15 min. step. As it was proven by the analysis, the oxygen content increased with increasing annealing time. Moreover, microhardness measurements showed increasing trend of HV microhardness value with increasing oxygen content.
Ključne riječi
titanium; oxygen content; microhardness