Izvorni znanstveni članak

Fatigue crack growth and fracture mechanics analysis of a working roll surface layer material

M. Drobne ; Valji, production of rolls and castings d.o.o., Slovenia
T. Vuherer ; University of Maribor, Faculty of Mechanical Engineering, Slovenia
I. Samardžić ; University of Osijek, Mechanical Engineering Faculty, Slavonski Brod, Croatia
S. Glodež ; University of Maribor, Faculty of Mechanical Engineering, Slovenia

Sažetak

Fatigue crack growth and fracture mechanics analysis of a working roll surface layer material is presented in this paper. The research is done on a hot strip mill working roll where High Chromium Steel is used for roll’s shell material. To obtain corresponding parameters, a rectangular single edge notched bend specimens – SENB, according to standard BS 7448, were used. The fatigue crack growth analysis was done on a resonant testing machine with use of special crack gauges, while for fracture mechanics parameters the electro–mechanical testing machine was used.

Ključne riječi

fracture mechanics; fatigue crack growth; rolling; high chromium steel

Hrčak ID:

122168

URI

https://hrcak.srce.hr/122168

Datum izdavanja:

1.10.2014.