Analysis of weld joints made of titanium alloy GRADE 2 produced by electron beam welding

J. Barta orcid.org/0000-0003-0607-4433 ; Faculty of Materials Sceicne and Technology, Slovak University of Technology, Trnava, Slovakia
M. Maronek orcid.org/0000-0002-4716-8092 ; Faculty of Materials Sceicne and Technology, Slovak University of Technology, Trnava, Slovakia
B. Šimekova ; Faculty of Materials Sceicne and Technology, Slovak University of Technology, Trnava, Slovakia
D. Marić ; Faculty of Mechanical Engine ering, Slavonski Brod, University of Osijek, Croatia

Sažetak

Selected properties of welded joints of 2 mm thick titanium alloy Grade 2 produced by different welding parameters of electron beam welding were investigated. The visual inspection, macro and micro analysis, tensile strength test and microhardness measurements were performed. Samples manufactured by appropriate welding parameters had no internal defects, heat-affected zone (HAZ) was narrow and transformation from α phase to β phase was observed in this area. The failure occurred in the base metal during tensile test, while maximum ultimate tensile strength reached 454,3 MPa.

Ključne riječi

titanium Grade2; electron beam welding; mechanical properties; structural analysis