Micromechanical properties of cryo-rolled (CR) aluminum alloy Al0,6Mg0,35Si
M. Abishkenov
orcid.org/0000-0002-7995-7651
; Karaganda Industrial University, Temirtau, Kazakhstan
Z. Ashkeyev
orcid.org/0000-0001-8992-3984
; Karaganda Industrial University, Temirtau, Kazakhstan
A. Naizabekov
; Rudny Industrial Institute, Rudny, Kazakhstan
K. Nogaev
orcid.org/0000-0003-1332-6352
; Karaganda Industrial University, Temirtau, Kazakhstan
L. Uktayeva
orcid.org/0000-0003-2901-6818
; Karaganda Industrial University, Temirtau, Kazakhstan
S. Kydyrbayeva
orcid.org/0000-0002-1664-237X
; Karaganda Industrial University, Temirtau, Kazakhstan
G. Issabekova
; Karaganda Industrial University, Temirtau, Kazakhstan
Abstract
The present study is devoted to the effect of cryorolling (– 150 °C) in mill rolls implementing shear alternating severe plastic deformation (SPD) on the microstructure and mechanical properties of the alloy. Comparison of the processes of cryorolling (CR) and rolling at room temperature (RTR) is given. The study of the microstructure of the samples and the mechanical properties showed that CR ensures the production of ultra-fine grained (UFG) material with an average grain size of 350 ÷ 500 nm, as well as an increase in hardness by 162,2 % (118 ± 2 HV) and Rm by 106,34 % (293 ± 5 MPa).
Keywords
Al0,6Mg0,35Si alloy; mechanical properties; cryorolling; transmission electron microscopy (TEM); UFG