Metalurgija, Vol. 62 No. 1, 2023.
Izvorni znanstveni članak
Research on promoting the formation and clusters of TiN phase in high purity cast iron
B. Dai
; Engineeing Research Institute of Anhui University of Technology, Maanshan, Anhui, China ; Key Laboratory of Metallurgical Emission Reduction & Resources Recycling, Anhui University of Technology, Ministry of Education, Maanshan, Anhui, China
Y. Ma
; Engineeing Research Institute of Anhui University of Technology, Maanshan, Anhui, China ; Key Laboratory of Metallurgical Emission Reduction & Resources Recycling, Anhui University of Technology, Ministry of Education, Maanshan, Anhui, China
F. Yu
; Wire works of Angang Steel Company Limited, Anshan, Liaoning, China
M. Yuan
; Engineeing Research Institute of Anhui University of Technology, Maanshan, Anhui, China ; Key Laboratory of Metallurgical Emission Reduction & Resources Recycling, Anhui University of Technology, Ministry of Education, Maanshan, Anhui, China
J. Chu
; Engineeing Research Institute of Anhui University of Technology, Maanshan, Anhui, China ; Key Laboratory of Metallurgical Emission Reduction & Resources Recycling, Anhui University of Technology, Ministry of Education, Maanshan, Anhui, China
Y. Xu
; Engineeing Research Institute of Anhui University of Technology, Maanshan, Anhui, China ; Key Laboratory of Metallurgical Emission Reduction & Resources Recycling, Anhui University of Technology, Ministry of Education, Maanshan, Anhui, China
Sažetak
As China is constantly striding forward from a large foundry country to a powerful one, the requirements of high purity cast iron for high-end castings have increased significantly and urgently. However, high purity cast iron produced by blast furnaces in China is always unable to meet national standard of high-end castings due to the exceeding of Ti. Based on the thermodynamic analysis, a detitanization method of increasing N in hot cast iron to promote the formation and clusters of TiN is proposed. High-temperature experiment has proved that N-addition can effectively promote the formation and clusters of TiN in hot cast iron, which provides the possibility for subsequent removal of Ti from high purity cast iron to meet the national standard.
Ključne riječi
cast iron; high purity; TiN; thermodynamic analysis; X-ray research (XRD, SEM, EDS)