Izvorni znanstveni članak
https://doi.org/10.15255/KUI.2018.037
The Influence of Heat Treatment on Microstructure and Phase Transformation Temperatures of Cu-Al-Ni Shape Memory Alloy
Ivana Ivanić
; Sveučilište u Zagrebu, Metalurški fakultet, Aleja narodnih heroja 3, 44 000 Sisak, Hrvatska
Stjepan Kožuh
; Sveučilište u Zagrebu, Metalurški fakultet, Aleja narodnih heroja 3, 44 000 Sisak, Hrvatska
Tamara Holjevac Grgurić
; Sveučilište u Zagrebu, Metalurški fakultet, Aleja narodnih heroja 3, 44 000 Sisak, Hrvatska
Borut Kosec
; Sveučilište u Ljubljani, Prirodoslovno-tehnički fakultet, Aškerčeva 12, 1000, Ljubljana, Slovenija
Mirko Gojić
; Sveučilište u Zagrebu, Metalurški fakultet, Aleja narodnih heroja 3, 44 000 Sisak, Hrvatska
Sažetak
This paper presents the results of thermal and microstructural analysis of Cu-Al-Ni shape memory alloy before and after heat treatment. After casting, a bar of Cu-12.8 Al-4.1 Ni (wt.%) alloy, obtained by the vertical continuous casting technique, was subjected to a certain heat treatment procedure. Solution annealing was performed at 850 °C for 60 min, followed by water quenching. Tempering was then performed at four different temperatures (150 °C, 200 °C, 250 °C and 300 °C). The microstructural results were obtained by optical and scanning electron microscopy. Thermodynamic calculation of ternary Cu-Al-Ni system under equilibrium was performed using Thermo-Calc 5 software. Phase transformation temperatures were determined by differential scanning calorimetry (DSC). The DSC results show the highest values of transformation temperatures in as-cast state. After solution annealing and tempering, the transformation temperatures show lower values with exceptional stability of Ms temperature (martensite start temperature).
This work is licensed under a Creative Commons Attribution 4.0 International License.
Ključne riječi
shape memory alloy; Cu-Al-Ni; heat treatment; phase transformation; microstructure