Hydrothermal Synthesis of Platinum Group Metal Nanoparticles

Stjepko Krehula orcid id orcid.org/0000-0001-6956-4478 ; Division of Materials Chemistry, Ruđer Bošković Institute, P.O. Box 180, HR-10002 Zagreb, Croatia
Svetozar Musić ; Division of Materials Chemistry, Ruđer Bošković Institute, P.O. Box 180, HR-10002 Zagreb, Croatia


Puni tekst: engleski pdf 6.009 Kb

str. 465-468

preuzimanja: 3.671

citiraj


Sažetak

A novel route for the synthesis of platinum group metal nanoparticles has been reported. The
synthesis is based on the addition of tetramethylammonium hydroxide (TMAH) to the aqueous PtCl4,
IrCl3 or Rh(NO3)3 solution followed by the hydrothermal treatment of these precipitation systems at
160 ºC. The mean size of nanoparticles was 9.2 nm for platinum, 21 nm for iridium, and 28 nm for rhodium.
The average crystallite size was estimated at 7.4 nm for platinum, 3.1 nm for iridium and 3.5 nm for
rhodium. The possible mechanism of platinum group metal nanoparticles formation is briefly discussed.
(doi: 10.5562/cca1856)

Ključne riječi

platinum; iridium; rhodium; nanoparticles; hydrothermal synthesis; tetramethylammonium hydroxide