Modeli za ispitivanje rastezne čvrstoće nisko-ugljičnih mikrolegiranih čelika s visokim sadržajem niobija
Marcos Pérez-Bahillo
; Materials Department, CEIT and Tecnun, University of Navarra, Paseo Manuel Lardizabal 15, 20018, San Sebastian, Spain
Nenad Gubeljak
; Faculty of Mechanical Engineering, University of Maribor, Smetanova 17, Maribor, Slovenia
David A. Porter
; Rautaruukki Oyj, Research Centre, P. O. Box 93, Raahe, Finland
Beatriz López
; Materials Department, CEIT and Tecnun, University of Navarra, Paseo Manuel Lardizabal 15, 20018, San Sebastian, Spain
Jožef Predan
; Faculty of Mechanical Engineering, University of Maribor, Smetanova 17, Maribor, Slovenia
Antonio Martín-Meizoso
; Materials Department, CEIT and Tecnun, University of Navarra, Paseo Manuel Lardizabal 15, 20018, San Sebastian, Spain
Sažetak
U ovom se istraživanju proučavao utjecaj parametara valjanja (2 redukcijske brzine i 3 brzine hlađenja) i kemijskih elemenata kao što su: C, Mn, Nb, Ti, Mo, Ni, Cr, Cu i B na svojstva čvrstoće niskougljičnih mikrolegiranih čelika s visokim sadržajem niobija (do 0,12 wt. % Nb). U tu je svrhu konstruiran pokusni uređaj zasnovan na inteligentnom dizajnu eksperimenata (DoE), rezultirajući s 26 odljevaka (laboratorijskih odljevaka). Kombinacijom metalografije, Electron Back-Scattered Diffraction (EBSD) i vlačnih ispitivanja proučavalo se kako obradni parametri i kemijski sastav djeluju na čvrstoću. Kada je ispitivanje rezultiralo naprezanjem, rasteznom čvrstoćom, jednoličnom deformacijom ili deformacijom zbog loma, rezultati su statistički analizirani tehnikom višestrukelinearne regresije, koja je dovela do odgovarajućih jednadžbi. Ustanovilo se da se učinak niobija na povećanje čvrstoće smanjuje kako se povećava sadržaj ugljika.
Ključne riječi
mikrolegirani čelici; mehanička svojstva; niobij