Wear intensity of diferent heat treated nodular cast irons

D. Golubović ; Faculty of Mechanical Engineering, East Sarajevo, Bosnia and Herzegovina
P. Kovač ; Faculty of Technical Science, University of Novi Sad, Serbia
D. Ješić ; Faculty of Engineering, University of Banja Luka, Bosnia and Herzegovina
M. Gostimirović ; Faculty of Technical Science, University of Novi Sad, Serbia
V. Pucovsky ; Faculty of Technical Science, University of Novi Sad, Serbia


Puni tekst: engleski pdf 886 Kb

verzije

str. 518-520

preuzimanja: 605

citiraj


Sažetak

In the paper we investigate the relationship between the wear intensity of two nodular cast irons and their heat treatment conditions. Disks tempered by austempering and isothermal procedure were used. The wear test was realized by using Pin and Disk tribometer. Measurement of the disks wear, after the contact for duration of 30 min, was done by the PQ meter. The quantity of the wear products in lubricant is determined by the PQ index. The best wear resistance posses the disk isothermally tempering with 30 minutes holding at 390 °C temperature.

Ključne riječi

nodular cast iron; wear; heat treatment