The Influence of Cyclic Loading on Ultimate Bending Strength of Beech Solid and Laminated Wood

Milan Gaff ; Odjel za namještaj i drvne proizvode, Fakultet za znanost o drvu i drvnu tehnologiju, Tehničko sveučilište, Zvolen, Republika Slovačka
Miroslav Gašparík orcid id orcid.org/0000-0002-0537-0815 ; Odjel za preradu drva, Fakultet šumarstva i znanosti o drvu, Češko sveučilište bioloških znanosti, Prag, Republika Češka
Štefan Barcík ; Odjel za preradu drva, Fakultet šumarstva i znanosti o drvu, Češko sveučilište bioloških znanosti, Prag, Republika Češka


Puni tekst: engleski pdf 681 Kb

str. 197-203

preuzimanja: 821

citiraj


Sažetak

This work investigates the influence of cyclic loading of beech solid and laminated wood of various thicknesses on ultimate bending strength (ultimate flexural strength) σp during bending in radial direction. For identification of ultimate bending strength, the static bending test with three-point loading was used. The ultimate bending strength was detected on testing samples that were not cyclically loaded and the results were compared with other results obtained from samples that were cyclically loaded. The results of this work show that the influence of cyclic loading on values of ultimate bending strength for solid and laminated wood is not significant. Thickness influence is a significant factor for both tested materials. The results show that the increase of thickness causes the decrease of ultimate bending strength. In our opinion, the decrease of ultimate bending strength is not caused by the sample thickness but by different sample lengths. With the increase of the sample length, the influence
of inhomogeneous wood properties also increases.

Ključne riječi

cyclic loading; laminated wood; solid wood; ultimate bending strength; beech wood; PVAC adhesive