The Analysis of Defects on Continuous Cast Billets

I. Mamuzić
M. Longauerova
A. Štrkalj


Puni tekst: engleski pdf 429 Kb

str. 201-207

preuzimanja: 8.737

citiraj


Sažetak

First the article presents the system of sampling and methods of correction of defects on continuous cast billets and rolled steel concrete bars. Although the chemical composition of these billets (with increased contents of manganese and oxygen) is adequate to the standard chemical composition (DIN 488 - BSt 500S) there are gas blow holes and cracks as well as central and peripheral segregation. The point is in unsatisfactory deoxidation of hot cracks which develop during solidification. A prove that the hot cracks are decarbonisation in cracks are inclusions of Si, MnS, Fe, S, respectively an increased content of accompanying elements. The hardness value indicates that the rolling process develops regularly, i.e. in the area of recrystallization of metal.

Ključne riječi

Hrčak ID:

127874

URI

https://hrcak.srce.hr/127874

Podaci na drugim jezicima: hrvatski

Posjeta: 8.991 *