Fatigue life of high strength steel for cold forming
; Institute of Production Engineering, Czestochowa University of Technology, Czestochowa, Poland
F. Novy ; Faculty of Mechanical Engineering, University of Zilina, Slovak Republic
Puni tekst: engleski pdf 413 Kb
APA 6th Edition
Ulewicz, R. i Novy, F. (2017). Fatigue life of high strength steel for cold forming. Metalurgija, 56 (1-2), 115-118. Preuzeto s https://hrcak.srce.hr/168902
MLA 8th Edition
Ulewicz, R. i F. Novy. "Fatigue life of high strength steel for cold forming." Metalurgija, vol. 56, br. 1-2, 2017, str. 115-118. https://hrcak.srce.hr/168902. Citirano 29.05.2023.
Chicago 17th Edition
Ulewicz, R. i F. Novy. "Fatigue life of high strength steel for cold forming." Metalurgija 56, br. 1-2 (2017): 115-118. https://hrcak.srce.hr/168902
Ulewicz, R., i Novy, F. (2017). 'Fatigue life of high strength steel for cold forming', Metalurgija, 56(1-2), str. 115-118. Preuzeto s: https://hrcak.srce.hr/168902 (Datum pristupa: 29.05.2023.)
Ulewicz R, Novy F. Fatigue life of high strength steel for cold forming. Metalurgija [Internet]. 2017 [pristupljeno 29.05.2023.];56(1-2):115-118. Dostupno na: https://hrcak.srce.hr/168902
R. Ulewicz i F. Novy, "Fatigue life of high strength steel for cold forming", Metalurgija, vol.56, br. 1-2, str. 115-118, 2017. [Online]. Dostupno na: https://hrcak.srce.hr/168902. [Citirano: 29.05.2023.]
The article presents the results of fatigue tests carried out on STRENX-type high-strength cold forming steel. For high-cycle fatigue tests carried out using low cycle loading frequencies of around 30 Hz, a ROTOFLEX machine was used. For ultra high-cycle tests, a KAUP-ZU testing machine was employed, which enables fatigue tests to be performed with symetric specimen loading (R = -1) and at a frequency of f ≈ 20 kHz. The relationships σa = f(N) were determined experimentally in the high and ultra high-cycle region for STRENX high-strength steel. To determine the fatigue crack initiation mechanism, the fractographic analysis of fatigue fractures was made.
high strength steel, ultra-high-cycle fatigue, Wöhler curve, fractography