Original scientific paper

Magnesite base desulfurizer of metallurgical physical chemistry research

G. D. Liu ; School of Material and Metallurgy, University of Science and Technology Liaoning, AnShan, China
K. Liu ; School of Material and Metallurgy, University of Science and Technology Liaoning, AnShan, China
F. Xing ; School of Material and Metallurgy, University of Science and Technology Liaoning, AnShan, China

Abstract

This topic put carbon thermal vacuum method in combination with magnesium based desulfurization technology with magnesite reduction of magnesium vapor directly on hot metal desulphurization. This is a new type of desulfurization technology, the retrieval related literature at home and abroad was not reported in the recent ten years, according to the relationship between heat of desulfurizer preparation MgO style content can reach 50 %.It was found that the desulfurizer sample with 50 % MgO content was in accordance with the requirements, without adding flux, but its viscosity did not meet the requirements; adding 1 % flux (CaF₂), the sample viscosity was significantly reduced, and about 1 400 °C sample viscosity suitable for hot metal pretreatment desulfurization.

Keywords

metallurgy; desulfurization; magnesite; heat of metal; viscosity