Corrosion resistance of the X6CrNiTi18-10 material exposed to a salt spray test

T. Šolić ; Faculty of Mechanical Engineering in Slavonski Brod, University of Osijek, Croatia
D. Marić ; Faculty of Mechanical Engineering in Slavonski Brod, University of Osijek, Croatia
I. Putnik ; Faculty of Mechanical Engineering in Slavonski Brod, University of Osijek, Croatia
I. Samardžić ; Faculty of Mechanical Engineering in Slavonski Brod, University of Osijek, Croatia


Puni tekst: engleski pdf 1.636 Kb

str. 307-310

preuzimanja: 395

citiraj


Sažetak

The research was focused on testing the corrosion resistance of the X6CrNiTi18-10 material. This material exhibits good corrosion resistance in the humid atmosphere, but with the occurrence of chloride inclusion in the same atmosphere, its corrosion resistance is drastically reduced. The X6CrNiTi18-10 material is austenitic stainless steel susceptible to pitting corrosion and this can cause problems during exploitation of the construction made of this material. In order to determine the likelihood of pitting corrosion occurrence, a light microscopy was performed on test samples that were exposed to the salt spray test chamber atmosphere, i.e. sprayed with a 5% sodium chloride solution (NaCl) at different time intervals.

Ključne riječi

steel X6CrNiTi18-10, corrosion resistance, salt spray test chamber/NaCl, time interval, light microscope