Investigation of the Effect of Using Activated Sludge Treated with Acetic Acid on Physical and Strength Properties of Recycled Pulp
Naghmeh Amani
; Islamic Azad University, Chalous branch, Department of Wood Science and Paper Technology, Chalous, Iran
Ramin Vaysi
; Islamic Azad University, Chalous branch, Department of Wood Science and Paper Technology, Chalous, Iran
Abdollah Najafi
; Islamic Azad University, Chalous branch, Department of Wood Science and Paper Technology, Chalous, Iran
Seyed Eshagh Ebadi
; Islamic Azad University, Chalous branch, Department of Wood Science and Paper Technology, Chalous, Iran
Sažetak
This study aimed to scrutinize chemical treatment of Mazandaran Wood and Paper mill activated sludge with 3 % acetic acid for the manufacture of environmentally eco-friendly bio composite. In this study, the paper pulp required was obtained from the waste newsprint paper. The activated sludge was treated in a beaker for 3 min in 3 % acetic acid and then in a water bath at 75 and 100 °C for 45 and 90 min. After that, the treated activated sludge was mixed and refi ned with waste newsprint paper pulp at ratios of 0, 5, 10, 15 and 20 %. The test specimens were prepared according to TAPPI standard and the physical properties (water absorption and porosity) and mechanical (tensile strength, tear strength, ring crush test, burst strength and folding strength) were measured. The results showed that the activated sludge treatment caused the increase in tear strength, ring crush test, burst strength and porosity as well as the decrease in water absorption, tensile strength and folding strength. FT-IR spectrum of the treated samples showed that the treatment with acetic acid strengthened and activated the functional groups on the surface of activated sludge fi bers. The activated sludge added at a level of 5 % at 100 °C for 90 min as well as at a level of 20 % at 75 °C for 45 min was more suitable than other treatments.
Ključne riječi
activated sludge; acetic acid; newsprint paper; eco-friendly bio composite; resistance features