Effect of iron oxide content on dephosphorization behavior of slag gasification

S. H. Wang
H. K. Sun ; Metallurgy and Energy College, North China University of Science and Technology, Tangshan, China. Tangshan Key Laboratory of Special Metallurgy and Material Manufacture, Tangshan, China
S. Tong ; Metallurgy and Energy College, North China University of Science and Technology, Tangshan, China. Tangshan Key Laboratory of Special Metallurgy and Material Manufacture, Tangshan, China
C. X. Li ; Metallurgy and Energy College, North China University of Science and Technology, Tangshan, China. Tangshan Key Laboratory of Special Metallurgy and Material Manufacture, Tangshan, China
Y. K. Xue ; Metallurgy and Energy College, North China University of Science and Technology, Tangshan, China. Tangshan Key Laboratory of Special Metallurgy and Material Manufacture, Tangshan, China
Y. Zhang ; Metallurgy and Energy College, North China University of Science and Technology, Tangshan, China. Tangshan Key Laboratory of Special Metallurgy and Material Manufacture, Tangshan, China

Sažetak

The coke reduction gasification dephosphorization experiments were conducted on converter slag with FeO contents of 15 %, 20 %, 30 % and 35 %, respectively. Thermodynamic calculations , Scanning Electron Eicroscope (SEM) and Energy Dispersive Spectrometer (EDS) showed that the actual reduction Gibbs free energy of P₂O₅ was less than that of FeO for the coke reduction converter slag product of P₂, and the reactive driving force of P₂O₅ was greater under high FeO conditions. With the increase of FeO content, the gasification dephosphorization rate showed a trend of increasing first and then decreasing. After gasification dephosphorization, the presence of the Fe phase will adsorb more P elements, so the high FeO content is beneficial to increase the P₂O₅ activity, which is conducive to the gasification dephosphorization reaction.

Ključne riječi

iron oxide; gasification dephosphorization; Gibbs free energy; converter slag; X-ray research