Effect of hot rolling reduction on microstructures and textures of grain oriented silicon steel

Y. Y. Shao ; College of Applied Technology, University of Science and Technology Liaoning, Anshan, Liaoning, China
Z. W. Jia ; Iron and Steel Research Institutes, Ansteel Co. Ltd., Anshan, Liaoning, China
Q. Guo ; Cold Rolling Silicon Plant, Ansteel Co. Ltd., Anshan, Liaoning, China

Sažetak

The effect of hot rolling reduction on microstructures and textures of grain oriented silicon steel was studied by optical microscopy (OM), zeiss ultra 55 Scanning electron microscope (SEM) and Electron backscatter diffraction (EBSD) technique respectively. The results indicate that the effect of hot rolling reduction on grain size of hot rolled and normalized sheets in surface layer is great, while the effect on grain size of primary recrystallized grain is little. The shear zone thickens with the finishing reduction decreases, moreover strong {111}<112> and {110}<001> textures can be obtained in hot rolled sheets. Combined with the previous research conclusions, it can be found that the rolling process of oriented silicon steel is contributed to the formation of texture, while the recrystallization process reduces the sharpness of the texture.

Ključne riječi

grain oriented silicon steel; hot rolling; reduction; microstructure; texture