Evaluation of the Effects of Local Heating on Springback Behaviour for AHSS Docol 1400 Sheet Metal

Gökhan Küçüktürk orcid.org/0000-0001-6727-3650 ; Gazi University, Engineering Faculty, Mechanical Engineering Department, Ankara, TURKEY
Mehmet Tahta orcid.org/0000-0001-8646-2908 ; Gazi University, Engineering Faculty, Mechanical Engineering Department, Ankara, TURKEY
Hakan Gürün orcid.org/0000-0001-6189-6830 ; Gazi University, Graduate School of Natural and Applied Sciences, Ankara, TURKEY
Ibrahim Karaağaç orcid.org/0000-0001-6727-3650 ; Gazi University, Technology Faculty, Manufacturing Engineering Department, Ankara, TURKEY

Sažetak

In this study, the impacts of the heating temperature and bending angle on springback were experimentally examined in the V-bending of Docol 1400 steel sheets. The bending angle (30°, 60°, 90° and 120°) and the temperature (Room Temperature-RT, 200°C, 300°C, 400°C, 500°C, 600°C) of the bending zone were determined as the variable experimental parameters. The springback was measured using a coordinate measuring machine (CMM). The springback was observed to decrease by 7.7% on average between RT and 200 ºC, to increase by 8% between 200 ºC and 300 ºC and by 18% between 300 ºC and 600 ºC. The material data used in the analyses were attained from the tensile test results conducted at different temperatures. The analysis shows that the springback values decreased linearly at elevated temperatures. It was seen that the mechanical properties of the material decreased within the temperature range of RT to 600ºC in the heated bending zone.

Ključne riječi

springback; V-bending; Docol 1400; bending angle; hardness