Studying titanium carbide effect on cast iron AChS-3 properties

Sv. S. Kvon ; Karaganda Technical University, Karaganda, Kazakhstan, Ural State University, Russia
Zh. N. Atambayev ; Karaganda Technical University, Karaganda, Kazakhstan, Ural State University, Russia
K. Yu. Okishev ; Karaganda Technical University, Karaganda, Kazakhstan, Ural State University, Russia
N. B. Aitbayev ; Karaganda Technical University, Karaganda, Kazakhstan, Ural State University, Russia


Puni tekst: engleski pdf 142 Kb

str. 265-267

preuzimanja: 158

citiraj


Sažetak

The paper presents the results of studying microhardness and tribological characteristics of antifriction cast iron grade AChS-3 after modification with titanium carbide. Titanium carbide has been used as a nanomodifier to change the structure parameters by forming additional crystallization centers. It has been established that introducing titanium carbide in the amount of 0,2-0,3 % by weight with dispersion of 0,3-0,5 μm leads to increasing its hardness and wear resistance by about 20 %, while the friction coefficient decreases by almost 2 times.

Ključne riječi

cast iron; titanium carbide; nanomodifier; аntifriction; hardness