Time-resolved photoluminescence spectra of (AlxGa1-x) 0.51In0.49P (x=0.29) alloy

Yi Jun Lu Lu ; Department of Physics, Xiamen University, Xiamen, 361 005, P. R. China
Yu Lin Gao ; Department of Physics, Xiamen University, Xiamen, 361 005, P. R. China
Jian Sheng Zheng ; Department of Physics, Xiamen University, Xiamen, 361 005, P. R. China
Zhi Gang Cai ; State Key Laboratory of Optoelectronic Materials and Technologies, Zhongshang University, Guangzhou, 510 275, P. R. China
Hai Yu Sang ; State Key Laboratory of Optoelectronic Materials and Technologies, Zhongshang University, Guangzhou, 510 275, P. R. China
Xue Ran Zeng ; State Key Laboratory of Optoelectronic Materials and Technologies, Zhongshang University, Guangzhou, 510 275, P. R. China

Sažetak

Measurements of time-resolved photoluminescence (TRPL) spectra were made in a study of the optical properties of partially ordered quaternary (AlxGa1-x)0.51In0.49P (x=0.29) alloy. Both excitation-wavelength dependence of lifetime and excitation-intensity dependence of lifetime show a wide distribution of carriers. In TRPL spectra measured at 300 K, a blue-shift of photoluminescence (PL) peaks in (AlxGa1-x)0.51In0.49P is observed. The phenomenon is in agreement with the Z-shaped temperature dependence of the PL peak. Possible origins of the blue-shift and Z-shaped behaviour of PL peak are presented.

Ključne riječi

quaternary (AlxGa1-x)0.51In0.49P alloy; III-V semiconductors; ordered alloys; photoluminescence