Nastanak koercitivnog polja pojačanog površinskim poljem u nanofaznoj traci fe73.5cu1nb3si15.5b7
Stjepan Sabolek
; Department of Physics, Faculty of Science, University of Zagreb, Bijenička 32, 10 000 Zagreb, Croatia
Emil Babić
; Department of Physics, Faculty of Science, University of Zagreb, Bijenička 32, 10 000 Zagreb, Croatia
Ivica Kušević
; Department of Physics, Faculty of Science, University of Zagreb, Bijenička 32, 10 000 Zagreb, Croatia
Marko Šušak
; Department of Physics, Faculty of Science, University of Zagreb, Bijenička 32, 10 000 Zagreb, Croatia
Dario Posedel
; Department of Physics, Faculty of Science, University of Zagreb, Bijenička 32, 10 000 Zagreb, Croatia
Denis Stanić
; Department of Physics, Faculty of Science, University of Zagreb, Bijenička 32, 10 000 Zagreb, Croatia
Sažetak
Proučavali smo utjecaj površinskih polja Hp (proizvedenih stalnom ili izmjeničnom strujom sredice) na meka magnetska svojstva amorfne i nanokristalinične trake Fe73.5Cu1Nb3Si15.5B7. Dok se koercitivno polje Hc u amorfonj traci smanjuje s Hp, u toj traci nakon najpovoljnijeg opuštanja (Hc = 1.3 A/m, Mm ≈ Ms) Hc raste s Hp, a gubici E zbog histerezne petlje smanjuju se s Hp za različita polja Hp (statičko, i dinamičko s različitim fazama u odnosu na magnetizirajuće polje H). Neočekivan porast Hc u nanokristalnoj traci povezuje se s utjecajem Hp na površinsku i osnovnu (unutarnju) domensku strukturu. Razvili smo model koji uključuje to međudjelovanje i objašnjava sve eksperimentalne rezultate. Raspravljamo moguće nepovoljne utjecaje vanjskih polja slične konfiguracije kao Hp na svojstva tih traka i predlažemo načine spriječavanja tih utjecaja.