Kinetics analysis of quenching phase transformation of 1Cr13 steel by thermal analysis

F. D. Wang orcid.org/0009-0005-0837-7018 ; Liaoning Provincial Key Laboratory of Energy Storage and Utilization, Yingkou Institute of Technology, Yingkou 115014, China *
Y. Zhao ; Yingkou Zhongwang Aluminum Co., LTD Liaoning, China *
L. Xue
G. L. Tan ; Liaoning Provincial Key Laboratory of Energy Storage and Utilization, Yingkou Institute of Technology, Yingkou 115014, China *
X. K. Li ; Anshan Yanping packaging products manufacturing Co., LTD *

* Dopisni autor.

Sažetak

Differential scanning calorimetry (DSC) was used to study the transformation process of 1Cr13 steel under quenching condition. The DSC curves were measured from 1 050 °C to room temperature at the cooling rate of 10, 20, 30, 50 °C /min, respectively. The Flynn-Wall-Ozawa method was used to obtain the activation energy of the transformation process of 1Cr13 steel under quenching condition. The kinetic mechanism functions of the transformation process of 1Cr13 steel under quenching condition were also investigated by Criado-Ortega methods. The results show that the activation energy is related to the phase transition fraction. It means the transformation process of 1Cr13 steel under quenching condition is not a simple one-step reaction but a complex multi-step reaction.

Ključne riječi

1Cr13 steel; quenching; transformation; differential scanning calorimetry; the activation energy