Damage Level Estimate of API J55 Steel for Welded Seam Casing Pipes
Živče ŠARKOĆEVIĆ
orcid.org/0000-0002-6805-9936
; Visoka tehnička škola strukovnih studija u Zvečanu, Zvečan, Srbija
Miodrag ARSIĆ
; Institut za ispitivanje materijala - IMS, Beograd, Srbija
Bojan MEĐO
; Tehnološko-metalurški fakultet Univerziteta u Beogradu, Beograd, Srbija
Dražan KOZAK
; Strojarski fakultet u Slavonskom Brodu Sveučilišta J. J. Strossmayera u Osijeku, Slavonski Brod, Hrvatska
Marko RAKIN
; Tehnološko-metalurški fakultet Univerziteta u Beogradu, Beograd, Srbija
Zijah BURZIĆ
; Vojnotehnički institut, Beograd, Srbija
Aleksandar SEDMAK
; Mašinski fakultet Univerziteta u Beogradu, Beograd, Srbija
Sažetak
The subject of this paper is investigation of the damage level of API J55 steel, used for manufacturing casing pipes by high frequency (HF) contact welding. The analysed pipe was withdrawn after about 70 000 hours of service in an oil drilling rig. Experimental analysis included determining the mechanical properties of the base material and welded joint, in particular the tensile and impact toughness testing. Fracture behaviour is examined by testing the modified compact tension (CT) specimens machined with a pre-crack in the base metal, weld metal and heat affected zone (HAZ).
The critical value of the stress intensity factor KIc is determined using the critical value of the J integral JIc. Fatigue crack growth rate and fatigue threshold stress intensity factor range are determined by three point bending tests of the Charpy specimens with a V-notch. The investigation conducted on specimens cut from the exploited pipe and the new pipe of the same grade revealed that material properties were not seriously altered during the analysed period of service.
Ključne riječi
Casing pipe; Damage level; High frequency contact welding; Pipe integrity