Electrowinning of Nickel from ammonical sulphate bath and effect of acetone on morphology of nickel deposit and its correlation with kinetic parameters

D. K. Borikar
S. S. Umare
S. G. Viswanath

Puni tekst: engleski pdf 849 Kb

str. 3-8

preuzimanja: 1.956



The electrodeposition of nickel from nickel sulphate bath was studied in ammonia medium. The electrolytic conditions for nickel deposition was optimized at room temperature. The effect of acetone on current efficiency, morphology, stability and particle size of deposited nickel powder was studied. The effect of organic additive Tribenzyl ammonium chloride (TBAC) on the morphology of nickel powder was also studied. The kinetics of electrodeposition was studied and the results were utilized in developing mathematical model. During electrodeposition the current efficiency was found to increase with increase in acetone concentration up to 15% V/V in bath solution. On further increase of acetone concentration in bath solution current efficiency decreases. The stability of the electrowon deposited nickel powder was found to be in the range of 85 to 89 %. Powder morphology was found to be dentritic, porous and irregular. The morphology was also found to be underdeveloped dentritic to rounded aggregate as the concentration of organic additive TBAC increases. The average particle size of the deposited powder was found to be decreasing as the concentration of the acetone increases. The average size of the particle is in the range of 13-16 m.

Ključne riječi

powder metallurgy, electrowinning, nickel powder

Hrčak ID:



Posjeta: 2.537 *