SEM, EDS i XPS analiza nanostrukturirane prevlake koja se stvara na leguri od NiTi biomaterijala plasma elektrolitičkom oksidacijom (PEO)
Krzysztof Rokosz
; Division of BioEngineering and Surface Electrochemistry, Faculty of Mechanical Engineering, Koszalin University of Technology, Racławicka 15-17, 75-620 Koszalin, Poland
Tadeusz Hryniewicz
; Division of BioEngineering and Surface Electrochemistry, Faculty of Mechanical Engineering, Koszalin University of Technology, Racławicka 15-17, 75-620 Koszalin, Poland
Steinar Raaen
; Department of Physics, Norwegian University of Science and Technology (NTNU), Realfagbygget E3-124 Høgskoleringen 5, NO 7491 Trondheim
Abstract
Plasma elektrolitička oksidacija (PEO) NiTi legure proučavana je u elektrolitu koji se uobičajeno sastojao od koncentrirane ortofosforične kiseline s dodatkom nitrata bakra II. Taj se PEO postupak primijenio za dobivanje nanostrukturirane prevlake na Nitinol površini. Metode analize površinskog sloja kao što su skeniranje elektronskim mikroskopom (SEM) s energetski disperzivnom rendgenskom spektroskopijom (EDS) i rendgenskom fotoelektronskom spektroskopijom (XPS), omogućile su određivanje strukture i sastava najočekivanijih prevlaka i otkrivanje uvjeta za njihovo dobivanje. Ustanovilo se da se porozna PEO prevlaka dobivena u elektrolitu koji je sadržavao bakreni nitrat u količini većoj od 1,6 mol/L sastoji uglavnom od fosfata bakra-titanija-nikla. Uz to, u usporedbi s matricom, karcinogeni nikal u prevlaci srećom se javlja u vrlo malim količinama, tj. ispod 1 at%.
Keywords
biomaterijali; prevlake; elektrokemijske metode; energetski disperzivna rendgenska spektroskopija (EDS); legura NiTi; rendgenska fotoelektronska spektroskopija (XPS)