Drvna industrija, Vol. 61 No. 3, 2010.
Original scientific paper
Effect of Sanding on Surface Properties of Medium Density Fiberboard
Nadir Ayrilmis
orcid.org/0000-0002-9991-4800
; Forestry Faculty, Istanbul University, Istanbul, Turkey
Zeki Candan
; Forestry Faculty, Istanbul University, Istanbul, Turkey
Turgay Akbulut
; Forestry Faculty, Istanbul University, Istanbul, Turkey
Ozgur Balkiz
; Central Anatolia Forestry Research Institute, Ankara, Turkey
Abstract
The objective of this research was to investigate the effects of sanding on the surface properties of the medium density fiberboard (MDF) panels made from Rhododendron ponticum L. wood. The MDF panels were sanded with different sizes of the sand paper grit: 60-, 60+80- or 60+80+120-grit. Surface absorption and surface roughness of the MDF panels were determined based on EN 382-1 standard and ISO 4287 by using a fi ne stylus profi lometer, respectively. Sessile water drop technique was used to determine contact angle values of the panel surface. The results indicated that sanding process improved the surface smoothness of the panels. However, the wettability and surface absorption of the panels were negatively affected by increasing grit size. The MDF surface sanded with 60-grit size had a lower contact angle, more wettable surface, compared to those that were sanded with 60+80+120-grit size. For example, the average contact angle value of the panels sanded with 60-grit sandpaper was 43.3° as compared to the panels sanded with 60+80+120-grit sand paper which was 76.1°. The rougher surface was more wettable and absorbent compared to smoother surface. Based on the fi ndings obtained from the present study, sanding has a signifi cant effect on the wettability, surface roughness, and surface absorption of the MDF panels, which could provide useful information on the bonding and finishing of the MDF panels.
Keywords
contact angle; medium density fiberboard (MDF); rhododendron (R.)ponticum L.; sanding; surface absorption; surface roughness; wettability