Investigations of the Compressive Behaviour of Veneer in Thickness Direction

Beate Buchelt orcid.org/0000-0003-4671-0852 ; Institute of Wood and Paper Technology, Technische Universität Dresden, Dresden, Germany
Alexander Pfriem orcid.org/0000-0001-6999-6182 ; Faculty of Wood Science and Technology, Eberswalde University for Sustainable Development - University of Applied Sciences, Eberswalde, Germany
André Wagenführ ; Institute of Wood and Paper Technology, Technische Universität Dresden, Dresden, Germany

Abstract

Compression tests were conducted with veneers in the thickness direction. Thereby differences between the stress-strain curves of veneers and other known stress-strain curves were observed. Based on microscopic studies during the compression, it was possible to describe the deformation behaviour of the veneer, and deviations from known, typical stress-strain curves were substantiated and explained. It was found that a considerable part of the strain occurs by straightening the veneer at a relatively low stress level due to the waved form of veneer sheets and specimens. A distinctive stress plateau has not been established.

Keywords

compression test; deformation; light microscope; stress-strain curve; veneer