Technical gazette, Vol. 22 No. 1, 2015.
Original scientific paper
https://doi.org/10.17559/TV-20140211130812
SEM/EDX, XPS, korozija i karakterizacija hrapavosti površine AISI 316L SS nakon elektrokemijske obrade u koncentriranoj HNO3
Krzysztof Rokosz
; Division of Surface Electrochemistry and Technology, Koszalin University of Technology, Racławicka 15-17, 75-620 Koszalin, Poland
Tadeusz Hryniewicz
; Division of Surface Electrochemistry and Technology, Koszalin University of Technology, Racławicka 15-17, 75-620 Koszalin, Poland
Steinar Raaen
; Physics Department NTNU, NO-7491 Trondheim, Norway
Jan Valiček
; Institute of Physics, Faculty of Mining and Geology, VŠB - Technical University of Ostrava, 17. listopadu 15/2172, 708 33 Ostrava-Poruba, Czech Republic
Abstract
U radu se opisuje površina nehrđajućeg čelika AISI 316L poslije elektrokemijske obrade u koncentriranoj HNO3. Obilježena je prametrima hrapavosti, ponašanjem kod zaštite od korozije i kemijskim sastavom površinskog sloja. Uobičajeno korišteni 2D i 3D parametri hrapavosti koji opisuju površinu nakon elektrokemijske obrade su sljedeći: Ra = 0,737 μm i Sa = 1,13 μm kao i Rq = 0,895 μm i Sq = 1,37 μm. Kod proučavanja korozije pasivna gustoća struje bila je 2,3×10−2 μA/cm2, potencijal točkaste korozije Epit = 1140 mV vs. SCE i mogućnost ponovnog pasiviziranja bio je 79 mV vs. SCE. U površinskom su sloju otkriveni spojevi željeza, kroma, molibdena, kobalta, mangana, kao i kalcija (zagađenost). Rezultati visoke rezolucije XPC spektra pokazali su da se većina pronađenih željeznih spojeva može opisati kao Fe2O3/FeOOH, a spojevi kroma kao Cr2O3/CrOOH. Molibden otkriven u površinskom sloju bio je uglavnom sa strukturom valencija šest (65 at%) i pet (17 at%).
Keywords
AISI 316L SS; elektrokemijska obrada; HNO3; XPS; značajke korozije; hrapavost površine