Original scientific paper

https://doi.org/10.5552/drind.2016.1441

Utjecaj poli(vinil acetata) s punilom od nanočestica gline i celuloznih nanovlakana na čvrstoću lijepljenja drva topole i običnog bora

Deniz Aydemir orcid.org/0000-0002-7484-2126 ; Bartin University, Faculty of Forestry, Department of Forest Industrial Engineering, Bartin, Turkey
Gökhan Gündüz orcid.org/0000-0002-2602-2211 ; Bartin University, Faculty of Forestry, Department of Forest Industrial Engineering, Bartin, Turkey
Nejla Aşık ; Bartin University, Faculty of Forestry, Department of Forest Industrial Engineering, Bartin, Turkey
Alice Wang ; Luleå University of Technology, Wood Technology, Skellefteå, Sweden

Abstract

Za istraživanje utjecaja različitih punila na svojstva poli(vinil acetata) (PVA) odabrana su celulozna nanovlakna (CNFs) i nanočestice gline (NC). Svojstva PVA kompozita istražena su termoanalizom (TGA/DTG), skeniranjem elektronskim mikroskopom (SEM) i određivanjem smicajne čvrstoće spoja (LJSS). Morfološke su studije pokazale da su skupine čestica zabilježene na SEM slikama pri težinskom udjelu CNFs i NC punila od 1, 2 i 4 %. Raspršena morfologija orijentacije čestica i valovi ravnomjerno su raspoređeni na površini kompozita. Iz analize utjecaja punila na termičku stabilnost može se zaključiti da NC ima veći utjecaj od CNFs-a, ovisno o težinskom udjelu punila. Smicajna čvrstoća spoja općenito se povećava nakon dodavanja CNFs i NC punila na PVA matricu. Prema tome, može se reći da PVA s CNFs i NC punilom ima veću učinkovitost lijepljenja i može se primijeniti u aplikacijama koje zahtijevaju veću čvrstoću lijepljenja.

Keywords

poli(vinilni acetat); celulozna nanovlakna (CNFs); nanočestice gline (NC); kompoziti s punilom od nanočestica; adhezija