Original scientific paper

Effect of CaO/SiO₂ ratio on melting property and strength of sinter with vanadium-titanium iron ore addition

S. T. Yang ; School of Metallurgy, Northeastern University, China
M. Zhou ; School of Metallurgy, Northeastern University, China
T. Jiang ; School of Metallurgy, Northeastern University, China
X. X. Xue ; School of Metallurgy, Northeastern University, China
P. N. Duan ; School of Metallurgy, Northeastern University, China
W. J. Zhang ; School of Metallurgy, Northeastern University, China

Abstract

Melting behavior is the precondition of liquid phase reaction, which is the foundation of sinter consolidation. Melting property measurement and sinter pot test were adopted to determine the melting temperature and strength of sinter with 13 % and 40 % vanadium-titanium ore addition at different CaO/SiO₂ ratio. The results showed that, the increasing CaO/SiO₂ ratio positively influences the melting property. Due to the difference of TiO₂ content, the influence of increasing CaO/SiO₂ ratio on strength appears in different curves which are not the same as prediction. The sinter strength variations were not only influenced by melting property, but also by mineral texture. The influences of TiO₂ on melting property, strength, mineral texture especially SFCA were still needed a further study.

Keywords

vanadium - titanium iron ore; CaO/SiO₂; strength; sinter; mineral texture