Original scientific paper

Research of the plastic deformation localization of bimetal

S. Barannikova orcid.org/0000-0001-5010-9969 ; Institute of Strength Physics and Materials Science of Siberian Branch Russian Academy of Sciences (ISPMS SB RAS), Tomsk, Russia
Yu. Li orcid.org/0000-0003-1759-9606 ; Institute of Strength Physics and Materials Science of Siberian Branch Russian Academy of Sciences (ISPMS SB RAS), Tomsk, Russia
L. Zuev ; Institute of Strength Physics and Materials Science of Siberian Branch Russian Academy of Sciences (ISPMS SB RAS), Tomsk, Russia

Abstract

The aim of this contribution was to study the localization of the plastic deformation of bimetal based on a low-carbon steel A 283 Grade C and austenitic stainless steel 301 AISI. The images of the localized zone plastic deformation upon the uniaxial tension have been obtained with using digital image correlation method (DIC). The stress-strain curves are found to show all the plastic flow stages: yield plateau, linear and parabolic work hardening stages and the prefracture stage would occur for the respective values of the exponent from the Ludwik-Holomon equation. The main parameters of plastic flow localization at various stages of the deformation hardening have been determined in bimetal.

Keywords

bimetal; localization of the plastic deformation; DIC; tensile test; strain