Assessment of the effectiveness of 316L austenitic steel unconventional glow discharge nitriding

T. Frączek ; Czestochowa University of Technology, Czestochowa, Poland
C. Kolmasiak ; Czestochowa University of Technology, Czestochowa, Poland
M. Olejnik ; Czestochowa University of Technology, Czestochowa, Poland
Z. Skuza ; Czestochowa University of Technology, Czestochowa, Poland


Full text: english pdf 520 Kb

page 97-100

downloads: 517

cite


Abstract

The 316L grade austenitic steel after glow discharge nitriding at a temperature of T=733 K for a duration of τ = 61,2 ks and four different variants of specimen arrangement in the glow-discharge chamber was investigated. In order to assess the effectiveness of nitriding process variants, the profile analysis examination of obtained surface layers, surface hardness tests and surface layer hardness profile examination, the analysis of surface layer structures and abrasive wear were performed. It has been found that an application of the booster screens causes depth increase of the nitrogen diffusion into the nitrided 316L austenitic steel and thus an increase of the obtained surface layers thickness.

Keywords

austenitic stainless steel; glow discharge nitriding; surface layer structure; hardness