Ellipsometric measurement of thickness of tin oxides grown by voltammetry in phosphate solution of pH 8.7

Tiago Brandão Costa orcid id orcid.org/0000-0003-3028-7965 ; Programa de Pós-Graduação em Engenharia Metalúrgica (PPGEM), Escola de Engenharia Industrial Metalúrgica de Volta Redonda (EEIMVR), Universidade Federal Fluminense (UFF), 27255-125 Volta Redonda, RJ, Brazil
Tania Maria Cavalcanti Nogueira ; Programa de Pós-Graduação em Engenharia Metalúrgica (PPGEM), Escola de Engenharia Industrial Metalúrgica de Volta Redonda (EEIMVR), Universidade Federal Fluminense (UFF), 27255-125 Volta Redonda, RJ, Brazil
Ladário da Silva ; Programa de Pós-Graduação em Engenharia Metalúrgica (PPGEM), Escola de Engenharia Industrial Metalúrgica de Volta Redonda (EEIMVR), Universidade Federal Fluminense (UFF), 27255-125 Volta Redonda, RJ, Brazil

Puni tekst: engleski pdf 1.385 Kb

str. 303-314

preuzimanja: 637

citiraj

Sažetak

The voltammetry induced growth of tin oxides on tin in the buffer solution of 0.18 mol L-1 Na2H2PO4 and 0.18 mol L-1 KH2PO4 (pH 8.7) has been studied. Ex-situ ellipsometric mea-surements were made in an order to determine thicknesses of the grown oxides. From these results the film volume per charge unit, Vf, was calculated for different charge den-sities of the film. This parameter was used to calculate the variable ionic resistivity of the film, ρf, considered by the Ohmic model for the case of voltammetric growth of oxides on metals having a previously existing continuous film. Tin oxide films grown at 2 mV s-1 showed to be less dense for values of charge density below 50 C m-2, having Vf near 5.7x10-10 m3 C-1. For higher values of charge density, tin oxide films become denser, having Vf near 0.5x10-10 m3 C-1. The calculated values of the variable ionic resistivity of the film during voltammetric growth showed that ρf passes through a minimum (justifying the maximum in current densities). This behavior was also found by other authors in the cases of Zn, Nb, Ni and galvanized steel sheets.

Ključne riječi

Ellipsometry; Tin oxide; Ohmic model; Voltammetry; Variable ionic resistivity