The study evolution of the structure formation of the foil workpiece during rolling screw rollers and longitudinal-wedge mill (LWM)

S. A. Mashekov ; Satbayev University, Almaty, Kazakhstan
G. A. Smailova ; Kazakh Agrarian University, Almaty, Kazakhstan
M. S. Kulgildinov ; Kazakh Academy of Transport and Communications named after M. Tynyshpayev, Almaty, Kazakhstan
K. T. Tergemes ; Almaty University of Power Engineering and Telecommunications, Almaty, Kazakhstan
A. Zhauyt ; Almaty University of Power Engineering and Telecommunications, Almaty, Kazakhstan
K. S. Chezhimbayeva ; Almaty University of Power Engineering and Telecommunications, Almaty, Kazakhstan
T. M. Buzauova ; Karaganda State Technical University, Kazakhstan

Sažetak

The article presents the results of studies of the influence number of passes and single crimps during rolling strips, respectively, in helical rolls and longitudinal-wedge mill on the parameters of the microstructure of aluminum alloy 2017. Comparative assessment grain sizes of ultrafine-grained structure after rolling strips with different passes in the helical rolls and deformation of the longitudinal-wedge mill at a deformation temperature of 400 °C. It is shown that the aluminum alloy sheet material 2017 provides the formation of a homogeneous ultrafine grain structure with a grain size of about 240 nm, which leads to an increase strength and plastic properties of the alloy.

Ključne riječi

aluminum alloy 2017; rolling; sheet; structure; temperature