Izvorni znanstveni članak
Termički utjecaj na JC q B q T plohe srebrom obloženih supravodljivih vrpci na osnovi bizmuta
Ivica Kušević
; Department of Physics, Faculty of Science, University of Zagreb, P.O. Box 162, HR-10001 Zagreb, Croatia
Emil Babić
; Department of Physics, Faculty of Science, University of Zagreb, P.O. Box 162, HR-10001 Zagreb, Croatia
Perica Šimundić
; Department of Physics, Faculty of Science, University of Zagreb, P.O. Box 162, HR-10001 Zagreb, Croatia
Jovica Ivkov
; Institute of Physics of the University, P.O. Box 304, HR-10001 Zagreb, Croatia
Željko Marohnić
; Institute of Physics of the University, P.O. Box 304, HR-10001 Zagreb, Croatia
Hua Kun Liu
; Centre of Superconducting and Electronic Materials, University of Wollongong, Wollongong, NSW2522, Australia
Shi Xue Dou
; Centre of Superconducting and Electronic Materials, University of Wollongong, Wollongong, NSW2522, Australia
Sažetak
Proučavane su Jc q B q T plohe srebrom obloženih Bi2Sr2CaCu2O8rx (Bi2212) i (Bi, Pb)2Sr2Ca2Cu3O10rx (Bi2223) vrpci u području temperatura 4.5 – 100 K i magnetskog polja B s 1 T. Jc t T u Bv i gustoća sile zapinjanja Fp w JcB, u obje vrste vrpci, pokazuju normiranje slično onom u monokristalima i epitaksijalnim slojevima visokotemperaturnih supravodiča, za temperature T s 0 x 5 Tc. Paralelno istraživanje potencijala zapinjanja U0 i ireverzibilnih polja Birr (određenih iz otpornih prijelaza u magnetskom polju) pokazuju da aktivacijske barijere U w U0 t 1 q T y Tc v y B m određuju veličine i temperaturne ovisnosti normirajućih polja Bz (definiranih s Fp w Fpmax) i Birr . Znatno veći U0 za Bi2223 traku u usporedbi s onim Bi2212 trake, pripisuje se nizoj anizotropiji tog spoja i višem stupnju strukturnih nesavršenosti. Međutim, u obje vrste vrpci zapinjanje magnetskih vrtloga nije dovoljno za njihove primjene u jakim poljima i pri visokim temperaturama.
Ključne riječi