Electrochemical behaviour of Ti6Al4V porous structures fabricated by powder metallurgy route

Maninder Singh ; Department of Mechanical Engineering, I. K. Gujral Punjab Technical University, Kapurthala, Punjab, India
Amoljit Singh Gill ; Mechanical Engineering Department, National Institute of Technology,Kurukshetra, Haryana, 136119, India
Parneet Kaur Deol ; Mechanical Engineering Department, Baba Banda Singh Bahadur Engineering College, Fatehgarh Sahib, Punjab,140407, India


Puni tekst: engleski pdf 1.130 Kb

str. 473-486

preuzimanja: 38

citiraj


Sažetak

In this investigation, the powder metallurgy process was used to fabricate porous structures of Ti6Al4V alloy by adding space holder powder particles. The samples were fabricated with varying levels of compaction pressure and other process parameters were kept unchanged in order to investigate the variation in electrochemical behaviour. It was observed that a lower level of compaction pressure resulted in an increase in corrosion current density and rate and a decrease in polarisation resistance. The sample's inability to achieve passivity against electrochemical corrosion, when fabricated using a lower level of compaction pressure, was linked to a higher number of interconnecting micropores. The results of the microstructure analysis confirmed the significant densification of the powder particles when higher compaction pressure was used. The study recommends that a compaction pressure of 300 MPa or higher may be used for fabricating porous structures for biomedical applications.

Ključne riječi

Titanium alloy; biomaterials; space holder; compaction pressure; corrosion