The effect of deformation on the change of hydrogen diffusion in C-Mn-Si-P Trip 800 steel

P. Váňová ; VŠB – Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, Czech Republic
J. Sojka ; VŠB – Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, Czech Republic
T. Kulová ; VŠB – Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, Czech Republic
V. Vodárek ; VŠB – Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, Czech Republic
M. Sozańska ; Silesian University of Technology, Faculty of Materials Engineering and Metallurgy, Katowice, Poland
B. Chmiela ; Silesian University of Technology, Faculty of Materials Engineering and Metallurgy, Katowice, Poland
J. Lelątko ; University of Silesia in Katowice, Faculty of Computer Science and Materials Science, Chorzów, Poland

Puni tekst: engleski, pdf (379 KB) str. 361-364 preuzimanja: 212* citiraj
APA 6th Edition
Váňová, P., Sojka, J., Kulová, T., Vodárek, V., Sozańska, M., Chmiela, B. i Lelątko, J. (2016). The effect of deformation on the change of hydrogen diffusion in C-Mn-Si-P Trip 800 steel. Metalurgija, 55 (3), 361-364. Preuzeto s https://hrcak.srce.hr/153620
MLA 8th Edition
Váňová, P., et al. "The effect of deformation on the change of hydrogen diffusion in C-Mn-Si-P Trip 800 steel." Metalurgija, vol. 55, br. 3, 2016, str. 361-364. https://hrcak.srce.hr/153620. Citirano 20.02.2019.
Chicago 17th Edition
Váňová, P., J. Sojka, T. Kulová, V. Vodárek, M. Sozańska, B. Chmiela i J. Lelątko. "The effect of deformation on the change of hydrogen diffusion in C-Mn-Si-P Trip 800 steel." Metalurgija 55, br. 3 (2016): 361-364. https://hrcak.srce.hr/153620
Harvard
Váňová, P., et al. (2016). 'The effect of deformation on the change of hydrogen diffusion in C-Mn-Si-P Trip 800 steel', Metalurgija, 55(3), str. 361-364. Preuzeto s: https://hrcak.srce.hr/153620 (Datum pristupa: 20.02.2019.)
Vancouver
Váňová P, Sojka J, Kulová T, Vodárek V, Sozańska M, Chmiela B i sur. The effect of deformation on the change of hydrogen diffusion in C-Mn-Si-P Trip 800 steel. Metalurgija [Internet]. 2016 [pristupljeno 20.02.2019.];55(3):361-364. Dostupno na: https://hrcak.srce.hr/153620
IEEE
P. Váňová, et al., "The effect of deformation on the change of hydrogen diffusion in C-Mn-Si-P Trip 800 steel", Metalurgija, vol.55, br. 3, str. 361-364, 2016. [Online]. Dostupno na: https://hrcak.srce.hr/153620. [Citirano: 20.02.2019.]

Sažetak
Hydrogen diffusion characteristics were studied in C - Mn - Si - P TRIP 800 steel. The steel was tested in as-received state and in states after 5 and 10 % tensile deformation. The steel microstructure consisted predominantly of ferrite, bainite and retained austenite. The tensile deformation resulted in a decrease of the retained austenite content. Hydrogen diffusion characteristics were studied by means of electrochemical permeation method for two current densities in build-up transients. Hydrogen diffusion coefficients of the studied TRIP steel varied from 1,6・10-7cm2・s-1 for the as-received state to 1,3・10-6 cm2・s-1 for the state after 5 % tensile deformation. The hydrogen diffusion coefficients increased markedly during the second build-up transient reflecting thus the fact that hydrogen trapping was less pronounced.

Ključne riječi
TRIP steel; deformation; hydrogen; diffusion; electrochemical permeation method