Processing of TiO2 from titanium-bearing blast furnace slag as titanium source

X. Li ; School of Material Science and Engineering, Shenyang Ligong University, Shenyang, China
H. H. Yu ; School of Material Science and Engineering, Shenyang Ligong University, Shenyang, China
Z. H. Fang ; School of Material Science and Engineering, Shenyang Ligong University, Shenyang, China
Z. G. Yuan ; School of Material Science and Engineering, Shenyang Ligong University, Shenyang, China
X. X. Xue ; School of Material and Metalurgy, Northeastern University, Shenyang, China

Puni tekst: engleski, pdf (286 KB) str. 379-381 preuzimanja: 486* citiraj
APA 6th Edition
Li, X., Yu, H.H., Fang, Z.H., Yuan, Z.G. i Xue, X.X. (2016). Processing of TiO2 from titanium-bearing blast furnace slag as titanium source. Metalurgija, 55 (3), 379-381. Preuzeto s https://hrcak.srce.hr/153624
MLA 8th Edition
Li, X., et al. "Processing of TiO2 from titanium-bearing blast furnace slag as titanium source." Metalurgija, vol. 55, br. 3, 2016, str. 379-381. https://hrcak.srce.hr/153624. Citirano 05.12.2019.
Chicago 17th Edition
Li, X., H. H. Yu, Z. H. Fang, Z. G. Yuan i X. X. Xue. "Processing of TiO2 from titanium-bearing blast furnace slag as titanium source." Metalurgija 55, br. 3 (2016): 379-381. https://hrcak.srce.hr/153624
Harvard
Li, X., et al. (2016). 'Processing of TiO2 from titanium-bearing blast furnace slag as titanium source', Metalurgija, 55(3), str. 379-381. Preuzeto s: https://hrcak.srce.hr/153624 (Datum pristupa: 05.12.2019.)
Vancouver
Li X, Yu HH, Fang ZH, Yuan ZG, Xue XX. Processing of TiO2 from titanium-bearing blast furnace slag as titanium source. Metalurgija [Internet]. 2016 [pristupljeno 05.12.2019.];55(3):379-381. Dostupno na: https://hrcak.srce.hr/153624
IEEE
X. Li, H.H. Yu, Z.H. Fang, Z.G. Yuan i X.X. Xue, "Processing of TiO2 from titanium-bearing blast furnace slag as titanium source", Metalurgija, vol.55, br. 3, str. 379-381, 2016. [Online]. Dostupno na: https://hrcak.srce.hr/153624. [Citirano: 05.12.2019.]

Sažetak
The titanium dioxide(TiO2) was prepared by efficient decomposition of titanium- bearing blast furnace slag (TBBFS) in molten salt system. The as-prepared TiO2 were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Almost complete leaching of Ti was achieved when TBBFS was carried out at 500 °C for about 3 h with NaOH/TBBFS mass ratio of 3:1 and NaOH to NaF molar ratio of 3:1. The XRD pattern showed that the containing titanium product obtained under optimal conditions was Na2TiO3. The average size of the rutile TiO2 obtained was about 1.0μm and the content was up to 99,23 %.

Ključne riječi
metallurgy; blast furnace; slag; TiO2; leaching