Determining the amount of Lüders band in niobium microalloyed steel

I. Jandrlić ; University of Zagreb, Faculty of Metallurgy, Sisak, Croatia
S. Rešković ; University of Zagreb, Faculty of Metallurgy, Sisak, Croatia
F. Vodopivec ; Institute of Metals and Technology, Ljubljana, Slovenia

Puni tekst: engleski, pdf (235 KB) str. 631-634 preuzimanja: 303* citiraj
APA 6th Edition
Jandrlić, I., Rešković, S. i Vodopivec, F. (2016). Determining the amount of Lüders band in niobium microalloyed steel. Metalurgija, 55 (4), 631-634. Preuzeto s https://hrcak.srce.hr/157384
MLA 8th Edition
Jandrlić, I., et al. "Determining the amount of Lüders band in niobium microalloyed steel." Metalurgija, vol. 55, br. 4, 2016, str. 631-634. https://hrcak.srce.hr/157384. Citirano 10.12.2019.
Chicago 17th Edition
Jandrlić, I., S. Rešković i F. Vodopivec. "Determining the amount of Lüders band in niobium microalloyed steel." Metalurgija 55, br. 4 (2016): 631-634. https://hrcak.srce.hr/157384
Harvard
Jandrlić, I., Rešković, S., i Vodopivec, F. (2016). 'Determining the amount of Lüders band in niobium microalloyed steel', Metalurgija, 55(4), str. 631-634. Preuzeto s: https://hrcak.srce.hr/157384 (Datum pristupa: 10.12.2019.)
Vancouver
Jandrlić I, Rešković S, Vodopivec F. Determining the amount of Lüders band in niobium microalloyed steel. Metalurgija [Internet]. 2016 [pristupljeno 10.12.2019.];55(4):631-634. Dostupno na: https://hrcak.srce.hr/157384
IEEE
I. Jandrlić, S. Rešković i F. Vodopivec, "Determining the amount of Lüders band in niobium microalloyed steel", Metalurgija, vol.55, br. 4, str. 631-634, 2016. [Online]. Dostupno na: https://hrcak.srce.hr/157384. [Citirano: 10.12.2019.]

Sažetak
The article presents the results of measuring the amount of deformation during the formation and propagation of Lüders bands through the deformation zone. The amount of deformation was determined by applying the visioplasticity method with digital image correlation, and analyzing the captured images using the MatchID software package. Results show that during the formation of Lüders bands, the deformation of 0,004 mm/mm was achieved. Furthermore, it was determined that during the propagation of Lüders bands through deformation zone, the sample was deformed in the amount of 0,05 mm/mm.

Ključne riječi
niobium microalloyed steel; plastic deformation; Lüders band; visioplasticity; digital image correlation