Studying intermetallic phase of Ni-Cr superalloy after thermal processing

A. Z. Issagulov ; Karaganda State Technical University, Karaganda, Kazakhstan
Sv. S. Kvon ; Karaganda State Technical University, Karaganda, Kazakhstan
V. Yu Kulikov ; Karaganda State Technical University, Karaganda, Kazakhstan
T. Kovalyova ; Karaganda State Technical University, Karaganda, Kazakhstan

Puni tekst: engleski, pdf (168 KB) str. 379-381 preuzimanja: 258* citiraj
APA 6th Edition
Issagulov, A.Z., Kvon, S.S., Kulikov, V.Y. i Kovalyova, T. (2017). Studying intermetallic phase of Ni-Cr superalloy after thermal processing. Metalurgija, 56 (3-4), 379-381. Preuzeto s https://hrcak.srce.hr/180988
MLA 8th Edition
Issagulov, A. Z., et al. "Studying intermetallic phase of Ni-Cr superalloy after thermal processing." Metalurgija, vol. 56, br. 3-4, 2017, str. 379-381. https://hrcak.srce.hr/180988. Citirano 28.01.2020.
Chicago 17th Edition
Issagulov, A. Z., Sv. S. Kvon, V. Yu Kulikov i T. Kovalyova. "Studying intermetallic phase of Ni-Cr superalloy after thermal processing." Metalurgija 56, br. 3-4 (2017): 379-381. https://hrcak.srce.hr/180988
Harvard
Issagulov, A.Z., et al. (2017). 'Studying intermetallic phase of Ni-Cr superalloy after thermal processing', Metalurgija, 56(3-4), str. 379-381. Preuzeto s: https://hrcak.srce.hr/180988 (Datum pristupa: 28.01.2020.)
Vancouver
Issagulov AZ, Kvon SS, Kulikov VY, Kovalyova T. Studying intermetallic phase of Ni-Cr superalloy after thermal processing. Metalurgija [Internet]. 2017 [pristupljeno 28.01.2020.];56(3-4):379-381. Dostupno na: https://hrcak.srce.hr/180988
IEEE
A.Z. Issagulov, S.S. Kvon, V.Y. Kulikov i T. Kovalyova, "Studying intermetallic phase of Ni-Cr superalloy after thermal processing", Metalurgija, vol.56, br. 3-4, str. 379-381, 2017. [Online]. Dostupno na: https://hrcak.srce.hr/180988. [Citirano: 28.01.2020.]

Sažetak
The superalloys on basis of Ni-Cr is meant for manufacturing rotor blades, disks and fastening details, which are used under 850 0С. These alloys additionally doped with Мо, Mo, W, Al and etc. for giving them a high-temperature properties. The main strengthening phase in these alloys is intermetallic phase, its nature, distribution pattern and dispersity [1].

Ključne riječi
Ni - Cr superalloy; thermal processing; melting; mechanical properties; metallographic analysis