A high-magnification EBSD mapping analysis of Fe–Si–B powder particles

M. Godec
B. Šuštaršič
M. Jenko

Puni tekst: engleski, pdf (1 MB) str. 9-12 preuzimanja: 945* citiraj
APA 6th Edition
Godec, M., Šuštaršič, B. i Jenko, M. (2008). A high-magnification EBSD mapping analysis of Fe–Si–B powder particles. Metalurgija, 47 (1), 9-12. Preuzeto s https://hrcak.srce.hr/17783
MLA 8th Edition
Godec, M., et al. "A high-magnification EBSD mapping analysis of Fe–Si–B powder particles." Metalurgija, vol. 47, br. 1, 2008, str. 9-12. https://hrcak.srce.hr/17783. Citirano 26.11.2020.
Chicago 17th Edition
Godec, M., B. Šuštaršič i M. Jenko. "A high-magnification EBSD mapping analysis of Fe–Si–B powder particles." Metalurgija 47, br. 1 (2008): 9-12. https://hrcak.srce.hr/17783
Harvard
Godec, M., Šuštaršič, B., i Jenko, M. (2008). 'A high-magnification EBSD mapping analysis of Fe–Si–B powder particles', Metalurgija, 47(1), str. 9-12. Preuzeto s: https://hrcak.srce.hr/17783 (Datum pristupa: 26.11.2020.)
Vancouver
Godec M, Šuštaršič B, Jenko M. A high-magnification EBSD mapping analysis of Fe–Si–B powder particles. Metalurgija [Internet]. 2008 [pristupljeno 26.11.2020.];47(1):9-12. Dostupno na: https://hrcak.srce.hr/17783
IEEE
M. Godec, B. Šuštaršič i M. Jenko, "A high-magnification EBSD mapping analysis of Fe–Si–B powder particles", Metalurgija, vol.47, br. 1, str. 9-12, 2008. [Online]. Dostupno na: https://hrcak.srce.hr/17783. [Citirano: 26.11.2020.]

Sažetak
We produced amorphous Fe–Si–B soft-magnetic powder using water atomisation. During annealing the powder particles developed a nanocrystalline structure, and annealing at over 700°C led to the formation of ferrite and boride phases. Here we present a high-magnification electron backscatter diffraction (EBSD) mapping analysis of the powder particles, in combination with a field-emission-gun scanning electron microscopy (FEGSEM) analysis. Some of the problems associated with the preparation of the powder particles for the EBSD analysis as well as the drift problems occurring during the EBSD mapping are reported.

Ključne riječi
EBSD; soft-magnetic materials; Fe–Si–B-based powder; nanocrystalline structure; amorphous