Heterogeneous nucleation of dicalcium phosphate dihydrate on modified silica surfaces
Carre Miller
Ljepša Komunjer
Vladimir Hlady
Sažetak
Heterogeneous nucleation of dicalcium phosphate dihydrate, CaHP04*2H,0 (DCPD) was studied on untreated planar fused silica and on three modified silica surfaces: octadecylsilyl (OTS) modified silica, human serum albumin treated OTS silica, and UV-oxidized 3 mercaptopropyltriethoxysilyl (MTS ) modified silica. The supersaturation ratio of calcium and phosphate solution with respect to DCPD was kept below -10. The nucleated crystals were observed 24 hours and one week after initial contact between supersaturated solutions and substrate surfaces using bright field and reflectance interference contrast microscopy. No DCPD crystals nucleated on albumin-treated OTS-silica. Majority of the DCDP crystals formed on the other modified silica surfaces appeared to be morphologically similar irrespective of the nature of nucleating substrate. Reflectance interference contrast microscopy provided a proof that the majority of the crystals on these substrates do not develop an extended contact with the substrate surface. The images showed that the most + extended contact planes were between the DCPD crystals and MTS modified silica surface. The crystals nucleated on OTS-treated and untreated silica surfaces showed only few or none well-developed contact planes.
Ključne riječi
Calcium phosphate; Dicalcium phosphate dihydrate; Heterogeneous nucleation theory; Microscopy - instrumentation, methods; Microscopy - reflectance interference contrast
Hrčak ID:
191892
URI
Datum izdavanja:
1.12.2010.
Posjeta: 721 *