F. Gapsari   ORCID icon orcid.org/0000-0003-3641-8372 ; Mechanical Engineering, Brawijaya University, Indonesia
Andoko ; Mechanical Engineering, State University of Malang, Indonesia
H. Wijaya ; Mechanical Engineering, Brawijaya University, Indonesia

Puni tekst: engleski, pdf (122 KB) str. 333-336 preuzimanja: 924* citiraj
APA 6th Edition
Gapsari, F., Andoko i Wijaya, H. (2018). Corrosion behavior of brass in nitric acid. Metalurgija, 57 (4), 333-336. Preuzeto s https://hrcak.srce.hr/201757
MLA 8th Edition
Gapsari, F., et al. "Corrosion behavior of brass in nitric acid." Metalurgija, vol. 57, br. 4, 2018, str. 333-336. https://hrcak.srce.hr/201757. Citirano 12.12.2019.
Chicago 17th Edition
Gapsari, F., Andoko i H. Wijaya. "Corrosion behavior of brass in nitric acid." Metalurgija 57, br. 4 (2018): 333-336. https://hrcak.srce.hr/201757
Harvard
Gapsari, F., Andoko, i Wijaya, H. (2018). 'Corrosion behavior of brass in nitric acid', Metalurgija, 57(4), str. 333-336. Preuzeto s: https://hrcak.srce.hr/201757 (Datum pristupa: 12.12.2019.)
Vancouver
Gapsari F, Andoko, Wijaya H. Corrosion behavior of brass in nitric acid. Metalurgija [Internet]. 2018 [pristupljeno 12.12.2019.];57(4):333-336. Dostupno na: https://hrcak.srce.hr/201757
IEEE
F. Gapsari, Andoko i H. Wijaya, "Corrosion behavior of brass in nitric acid", Metalurgija, vol.57, br. 4, str. 333-336, 2018. [Online]. Dostupno na: https://hrcak.srce.hr/201757. [Citirano: 12.12.2019.]

Sažetak
This research is a preliminary study of which purpose is to find some information about corrosion behavior of brass casted product in nitric acid. The corrosion rate test was conducted by polarization and Electrochemical Impedance Spectroscopy (EIS). This study was run with the variation of nitric acid of 0,5; 1; 1,5; 2 M. Optical Microscope (OM) were used to explain and to confirm polarization and EIS result. A mechanism for the reactions taking place at the electrode/electrolyte interface was explained.

Ključne riječi
corrosion; brass; EIS; nitric acid; polarization