Comparison of abrasion resistance of boron- and vanadium-based coatings

G. Heffer ; Faculty of Agrobiotechnical Sciences Osijek, Croatia
I. Samardžić ; Faculty of Mechanical Engineering Slavonski Brod, Croatia
I. Vidaković ; Faculty of Agrobiotechnical Sciences Osijek, Croatia
I. Opačak ; Faculty of Mechanical Engineering Slavonski Brod, Croatia

Puni tekst: engleski, pdf (2 MB) str. 247-250 preuzimanja: 268* citiraj
APA 6th Edition
Heffer, G., Samardžić, I., Vidaković, I. i Opačak, I. (2019). Comparison of abrasion resistance of boron- and vanadium-based coatings. Metalurgija, 58 (3-4), 247-250. Preuzeto s https://hrcak.srce.hr/218392
MLA 8th Edition
Heffer, G., et al. "Comparison of abrasion resistance of boron- and vanadium-based coatings." Metalurgija, vol. 58, br. 3-4, 2019, str. 247-250. https://hrcak.srce.hr/218392. Citirano 24.10.2021.
Chicago 17th Edition
Heffer, G., I. Samardžić, I. Vidaković i I. Opačak. "Comparison of abrasion resistance of boron- and vanadium-based coatings." Metalurgija 58, br. 3-4 (2019): 247-250. https://hrcak.srce.hr/218392
Harvard
Heffer, G., et al. (2019). 'Comparison of abrasion resistance of boron- and vanadium-based coatings', Metalurgija, 58(3-4), str. 247-250. Preuzeto s: https://hrcak.srce.hr/218392 (Datum pristupa: 24.10.2021.)
Vancouver
Heffer G, Samardžić I, Vidaković I, Opačak I. Comparison of abrasion resistance of boron- and vanadium-based coatings. Metalurgija [Internet]. 2019 [pristupljeno 24.10.2021.];58(3-4):247-250. Dostupno na: https://hrcak.srce.hr/218392
IEEE
G. Heffer, I. Samardžić, I. Vidaković i I. Opačak, "Comparison of abrasion resistance of boron- and vanadium-based coatings", Metalurgija, vol.58, br. 3-4, str. 247-250, 2019. [Online]. Dostupno na: https://hrcak.srce.hr/218392. [Citirano: 24.10.2021.]

Sažetak
This research focuses on testing of abrasion resistance of boron- and vanadium-based coatings. Coating of samples with vanadium was completed by classic and duplex procedure with previous carburization. The samples were abraded by applying the ASTM G65-94 method of „dry sand/rubber wheel“. The greatest wear was recorded on boron- based coating, and the least wear was exhibited by the vanadium-based coating with previous carburization. The dominant form of „zero“ abrasion was determined by analyzing the sample wear traces.

Ključne riječi
coatings; abrasion; microstructure; boronizing; vanadiumization