Change in the Microstructure of AlSi10MgMn Alloy with Higher Iron Content Due to an Increase in the Amount of Nickel

Mária Žihalová ; University of Žilina, Faculty of Mechanical Engineering, Department of Technological Engineering, Univerzitná 1, 010 26 Žilina
Dana Bolibruchová*   ORCID icon orcid.org/0000-0002-7374-9763 ; University of Žilina, Faculty of Mechanical Engineering, Department of Technological Engineering, Univerzitná 1, 010 26 Žilina
Marek Matejka   ORCID icon orcid.org/0000-0002-4156-5521 ; University of Žilina, Faculty of Mechanical Engineering, Department of Technological Engineering, Univerzitná 1, 010 26 Žilina

Puni tekst: engleski, pdf (2 MB) str. 34-37 preuzimanja: 48* citiraj
APA 6th Edition
Žihalová, M., Bolibruchová*, D. i Matejka, M. (2021). Change in the Microstructure of AlSi10MgMn Alloy with Higher Iron Content Due to an Increase in the Amount of Nickel. Tehnički vjesnik, 28 (1), 34-37. https://doi.org/10.17559/TV-20150513155430
MLA 8th Edition
Žihalová, Mária, et al. "Change in the Microstructure of AlSi10MgMn Alloy with Higher Iron Content Due to an Increase in the Amount of Nickel." Tehnički vjesnik, vol. 28, br. 1, 2021, str. 34-37. https://doi.org/10.17559/TV-20150513155430. Citirano 20.04.2021.
Chicago 17th Edition
Žihalová, Mária, Dana Bolibruchová* i Marek Matejka. "Change in the Microstructure of AlSi10MgMn Alloy with Higher Iron Content Due to an Increase in the Amount of Nickel." Tehnički vjesnik 28, br. 1 (2021): 34-37. https://doi.org/10.17559/TV-20150513155430
Harvard
Žihalová, M., Bolibruchová*, D., i Matejka, M. (2021). 'Change in the Microstructure of AlSi10MgMn Alloy with Higher Iron Content Due to an Increase in the Amount of Nickel', Tehnički vjesnik, 28(1), str. 34-37. https://doi.org/10.17559/TV-20150513155430
Vancouver
Žihalová M, Bolibruchová* D, Matejka M. Change in the Microstructure of AlSi10MgMn Alloy with Higher Iron Content Due to an Increase in the Amount of Nickel. Tehnički vjesnik [Internet]. 2021 [pristupljeno 20.04.2021.];28(1):34-37. https://doi.org/10.17559/TV-20150513155430
IEEE
M. Žihalová, D. Bolibruchová* i M. Matejka, "Change in the Microstructure of AlSi10MgMn Alloy with Higher Iron Content Due to an Increase in the Amount of Nickel", Tehnički vjesnik, vol.28, br. 1, str. 34-37, 2021. [Online]. https://doi.org/10.17559/TV-20150513155430

Sažetak
Recycling of the materials often requires modification of the manufacturing processes or application of the techniques to eliminate impurities that enter the material during recycling process. The main and the most detrimental impurity of the secondary (recycled) aluminium alloy is iron. Low iron solubility in aluminium leads to formation of the significant amount of harmful intermetallic phases that decrease foundry and mechanical properties of the final castings. Elimination of the detrimental iron effects might be achieved by addition of some chemical elements to change morphology of the intermetallic phase or to reduce negative effects of the phase to alloy properties. Gradual increase in the amount of nickel in the AlSi10MgMn alloy with a higher iron content is described in the presented article. From the selected additions of nickel (0,1, 0,3 and 0,5 wt.% Ni), the most favourable results were achieved by the addition of 0,5 wt. % Ni. Structural analysis of all experimental alloys (without addition and with a gradual addition of Ni) and related changes in measuring tensile and hardness properties is present.

Ključne riječi
Al-Si-Mg alloy; correctors of iron; nickel addition; recycled materials; structural analysis