Tribocorrosion of low carbon steel C15E IN 5% NaCl and 5% NaCl + SiO2

S. Aračić ; University of Osijek, Faculty of Mechanical Engineering, Slavonski Brod, Croatia
D. Krumes ; University of Osijek, Faculty of Mechanical Engineering, Slavonski Brod, Croatia
I. Vitez ; University of Osijek, Faculty of Mechanical Engineering, Slavonski Brod, Croatia

Puni tekst: engleski, pdf (1 MB) str. 111-114 preuzimanja: 510* citiraj
APA 6th Edition
Aračić, S., Krumes, D. i Vitez, I. (2010). Tribocorrosion of low carbon steel C15E IN 5% NaCl and 5% NaCl + SiO2. Metalurgija, 49 (2), 111-114. Preuzeto s https://hrcak.srce.hr/43653
MLA 8th Edition
Aračić, S., et al. "Tribocorrosion of low carbon steel C15E IN 5% NaCl and 5% NaCl + SiO2." Metalurgija, vol. 49, br. 2, 2010, str. 111-114. https://hrcak.srce.hr/43653. Citirano 21.09.2019.
Chicago 17th Edition
Aračić, S., D. Krumes i I. Vitez. "Tribocorrosion of low carbon steel C15E IN 5% NaCl and 5% NaCl + SiO2." Metalurgija 49, br. 2 (2010): 111-114. https://hrcak.srce.hr/43653
Harvard
Aračić, S., Krumes, D., i Vitez, I. (2010). 'Tribocorrosion of low carbon steel C15E IN 5% NaCl and 5% NaCl + SiO2', Metalurgija, 49(2), str. 111-114. Preuzeto s: https://hrcak.srce.hr/43653 (Datum pristupa: 21.09.2019.)
Vancouver
Aračić S, Krumes D, Vitez I. Tribocorrosion of low carbon steel C15E IN 5% NaCl and 5% NaCl + SiO2. Metalurgija [Internet]. 2010 [pristupljeno 21.09.2019.];49(2):111-114. Dostupno na: https://hrcak.srce.hr/43653
IEEE
S. Aračić, D. Krumes i I. Vitez, "Tribocorrosion of low carbon steel C15E IN 5% NaCl and 5% NaCl + SiO2", Metalurgija, vol.49, br. 2, str. 111-114, 2010. [Online]. Dostupno na: https://hrcak.srce.hr/43653. [Citirano: 21.09.2019.]

Sažetak
The article represents testing results of corrosion and erosion-corrosion wear. Specimens have been made from low carbon steel C15E in four different states: delivery state and heat-treated (carburizing, boronising and carburizing + boronising). The results are shown as wear of materials (losing of surface mass in mg/(cm2 • d)). Surface hardness method HV1 and micro hardness per section of specimen HV0,2 method have been used during the analyses. A comparison of testing results of wear in four different states was made. The best performances have shown samples which have been treated with duplex procedure (carburizing + boronising) as was predicted.

Ključne riječi
erosion - corrosion wear; low carbon steel; carburizing; boronising; duplex procedure