Credibility of various plastometric methods in simulation of hot rolling of the steel round bar

P. Kawulok ; VŠB – Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, Czech Republic
R. Kawulok ; VŠB – Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, Czech Republic
I. Schindler ; VŠB – Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, Czech Republic
S. Rusz ; VŠB – Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, Czech Republic
J. Kliber ; VŠB – Technical University of Ostrava, Faculty of Metallurgy and Materials Engineering, Czech Republic
P. Unucka ; Material and Metallurgical Research Ltd., Czech Republic
K. M. Čmiel ; Třinecké železárny a.s., Czech Republic


Puni tekst: engleski pdf 1.144 Kb

str. 299-302

preuzimanja: 643

citiraj


Sažetak

Rolling of round bar made of steel 32CrB4 was simulated physically. The interrupted torsion test led to the final microstructure with coarser grains, however, thanks to comparatively large dimensions of the sample this type of experiment was not so sensitive to the cooling rate of the final cooling as compression test. Too high temperature of the end of controlled cooling of the samples after compression test led to partial self-quenching of the investigated material. Decelerated cooling below the temperature of the start of martensitic transformation led in both applied types of compression tests to the parameters of the resulting microstructure and hardness closest to the parameters obtained after laboratory rolling.

Ključne riječi

laboratory hot rolling; metallographic analysis; torsion test; compression tests