Role of Cr and P Additions in the Development of Microstructure

E. V. Pereloma
I. B. Timokhina
A. I. Nosenkov
J. J. Jonas

Puni tekst: engleski, pdf (265 KB) str. 149-154 preuzimanja: 124* citiraj
APA 6th Edition
Pereloma, E.V., Timokhina, I.B., Nosenkov, A.I. i Jonas, J.J. (2004). Role of Cr and P Additions in the Development of Microstructure. Metalurgija, 43 (3), 149-154. Preuzeto s https://hrcak.srce.hr/128241
MLA 8th Edition
Pereloma, E. V., et al. "Role of Cr and P Additions in the Development of Microstructure." Metalurgija, vol. 43, br. 3, 2004, str. 149-154. https://hrcak.srce.hr/128241. Citirano 13.07.2020.
Chicago 17th Edition
Pereloma, E. V., I. B. Timokhina, A. I. Nosenkov i J. J. Jonas. "Role of Cr and P Additions in the Development of Microstructure." Metalurgija 43, br. 3 (2004): 149-154. https://hrcak.srce.hr/128241
Harvard
Pereloma, E.V., et al. (2004). 'Role of Cr and P Additions in the Development of Microstructure', Metalurgija, 43(3), str. 149-154. Preuzeto s: https://hrcak.srce.hr/128241 (Datum pristupa: 13.07.2020.)
Vancouver
Pereloma EV, Timokhina IB, Nosenkov AI, Jonas JJ. Role of Cr and P Additions in the Development of Microstructure. Metalurgija [Internet]. 2004 [pristupljeno 13.07.2020.];43(3):149-154. Dostupno na: https://hrcak.srce.hr/128241
IEEE
E.V. Pereloma, I.B. Timokhina, A.I. Nosenkov i J.J. Jonas, "Role of Cr and P Additions in the Development of Microstructure", Metalurgija, vol.43, br. 3, str. 149-154, 2004. [Online]. Dostupno na: https://hrcak.srce.hr/128241. [Citirano: 13.07.2020.]

Sažetak
The recrystallisation behaviour of four warm rolled steels was investigated during annealing. The extra-low carbon (ELC) steel displayed the highest rate of recrystallisation, the steels with additions of chromium and phosphorus (LC(Cr)), (LC(Cr,P)) recrystallised at intermediate rates, while the interstitial-free (IF) steel exhibited the lowest rate. The additions of Cr and Cr/P increased the fraction of g-fibre in the annealing textures compared to that present in the ELC steel; this effect was particularly pronounced up to 50 % recrystallisation. After the completion of recrystallisation, the steel textures were characterized by a dominant g-fibre in the IF steel, while in the three LC steels, the RD fibre was the principal one.